压水堆主回路高温水中奥氏体不锈钢加工表面的腐蚀与应力腐蚀裂纹萌生：研究进展及展望
Corrosion and Stress Corrosion Crack Initiation in the Machined Surfaces of Austenitic Stainless Steels in Pressurized Water Reactor Primary Water： Research Progress and Perspective
压水堆主回路高温水中奥氏体不锈钢加工表面的腐蚀与应力腐蚀裂纹萌生：研究进展及展望 |
| 常立涛 |
|
Corrosion and Stress Corrosion Crack Initiation in the Machined Surfaces of Austenitic Stainless Steels in Pressurized Water Reactor Primary Water： Research Progress and Perspective |
| CHANG Litao |
| 图3 砂纸磨抛在不锈钢表面引入的变形层的显微组织[ |
| Fig.3 BSE and BF-TEM images showing the microstructure of the deformation layer on ASSs induced by grinding using 800 grit (a)[ |
|
|