600℃ NaCl盐雾环境下GH4169合金的腐蚀行为
Corrosion Behavior of GH4169 Alloy in NaCl Solution Spray Environment at 600oC
600℃ NaCl盐雾环境下GH4169合金的腐蚀行为 |
| 张伟东, 崔宇, 刘莉, 王文泉, 刘叡, 李蕊, 王福会 |
|
Corrosion Behavior of GH4169 Alloy in NaCl Solution Spray Environment at 600oC |
| ZHANG Weidong, CUI Yu, LIU Li, WANG Wenquan, LIU Rui, LI Rui, WANG Fuhui |
| 图10 GH4169合金在600℃固态NaCl + 含O2水蒸汽环境腐蚀 20 h后内腐蚀区域的TEM像及EDS结果 |
| Fig.10 TEM image of internal corrosion scale of GH4169 alloy exposed in solid NaCl in wet O2 environment at 600oC for 20 h (a), and corresponding high magnified images of areas 1 (b) and 2 (c) in Fig.10a, respectively, and STEM-EDS result of Fig.10b (d) |
|
|