W含量对Ti-42Al-5Mn-xW合金相转变行为的影响
Effect of W Content on the Phase Transformation Behavior in Ti-42Al-5Mn- xW Alloy
W含量对Ti-42Al-5Mn-xW合金相转变行为的影响 |
| 李小兵, 潜坤, 舒磊, 张孟殊, 张金虎, 陈波, 刘奎 |
|
Effect of W Content on the Phase Transformation Behavior in Ti-42Al-5Mn- xW Alloy |
| LI Xiaobing, QIAN Kun, SHU Lei, ZHANG Mengshu, ZHANG Jinhu, CHEN Bo, LIU Kui |
| 图5 Ti-42Al-5Mn-xW合金1300℃处理1 h后以不同方式冷却的BSE像 |
| Fig.5 BSE images of Ti-42Al-5Mn-xW alloys with x = 0 (a1-a3), x = 0.5 (b1-b3), x = 0.8 (c1-c3), and x = 1.0 (d1-d3) after annealing at 1300oC for 1 h and then WC (a1-d1), AC (a2-d2), and FC (a3-d3) (Insets in Figs.5a1-d1 show the high magnified images) |
|
|