W含量对Ti-42Al-5Mn-xW合金相转变行为的影响
Effect of W Content on the Phase Transformation Behavior in Ti-42Al-5Mn- xW Alloy
W含量对Ti-42Al-5Mn-xW合金相转变行为的影响 |
| 李小兵, 潜坤, 舒磊, 张孟殊, 张金虎, 陈波, 刘奎 |
|
Effect of W Content on the Phase Transformation Behavior in Ti-42Al-5Mn- xW Alloy |
| LI Xiaobing, QIAN Kun, SHU Lei, ZHANG Mengshu, ZHANG Jinhu, CHEN Bo, LIU Kui |
| 图2 Ti-42Al-5Mn-0.5W合金不同温度保温1 h水淬后的BSE像 |
| Fig.2 Back scattering electron (BSE) images of Ti-42Al-5Mn-0.5W alloy after annealing at 1160oC (a), 1170oC (b), 1180oC (c), 1210oC (d), 1220oC (e), 1230oC (f), 1320oC (g), and 1330oC (h) for 1 h，and then water cooling (WC) (γg—γ grain, γlamellae—γ lamellae) |
|
|