GH3600镍基高温合金极薄带的制备及尺寸效应
Preparation and Size Effect of GH3600 Nickel-Based Superalloy Ultra-Thin Strips
GH3600镍基高温合金极薄带的制备及尺寸效应 |
| 于少霞, 王麒, 邓想涛, 王昭东 |
|
Preparation and Size Effect of GH3600 Nickel-Based Superalloy Ultra-Thin Strips |
| YU Shaoxia, WANG Qi, DENG Xiangtao, WANG Zhaodong |
| 图9 不同温度退火后0.125 mm厚GH3600镍基高温合金带材拉伸断口形貌的SEM像 |
| Fig.9 Low (a1-d1) and locally high (a2-d2) SEM images showing tensile fracture morphologies of 0.125 mm thick GH3600 nickel-based superalloy strips after annealing at 800oC (a1, a2), 900oC (b1, b2), 1000oC (c1, c2), and 1050oC (d1, d2) |
|
|