GH3600镍基高温合金极薄带的制备及尺寸效应
Preparation and Size Effect of GH3600 Nickel-Based Superalloy Ultra-Thin Strips
(a) 800oC, 0.25 mm (b) 800oC, 0.125 mm (c) 800oC, 0.07 mm
(d) 1050oC, 0.25 mm (e) 1050oC, 0.125 mm (f) 1050oC, 0.07 mm
GH3600镍基高温合金极薄带的制备及尺寸效应 |
| 于少霞, 王麒, 邓想涛, 王昭东 |
|
Preparation and Size Effect of GH3600 Nickel-Based Superalloy Ultra-Thin Strips |
| YU Shaoxia, WANG Qi, DENG Xiangtao, WANG Zhaodong |
| 图6 经不同退火温度处理的不同厚度GH3600镍基高温合金带材的带对比(BC)和晶界(GB)叠加图 |
| Fig.6 Bound contrast (BC) + grain boundry (GB) overlap diagrams of GH3600 nickel-based superalloys strips with different thicknesses treated at different annealing temperatures (High angle grain boundaries are shown in red lines, twin boundaries are shown in green lines, and the low angle grain boundaries are shown in blue lines) (a) 800oC, 0.25 mm (b) 800oC, 0.125 mm (c) 800oC, 0.07 mm (d) 1050oC, 0.25 mm (e) 1050oC, 0.125 mm (f) 1050oC, 0.07 mm |
|
|