露点对连续退火0.2%C-1.5%Si-2.5%Mn高强钢选择性氧化及脱碳的影响
Effect of Dew Point on Selective Oxidation and Decarburization of 0.2%C-1.5%Si-2.5%Mn High Strength Steel Sheet During Continuous Annealing
(a) upper zone (b) middle zone (c) bottom zone
露点对连续退火0.2%C-1.5%Si-2.5%Mn高强钢选择性氧化及脱碳的影响 |
| 金鑫焱, 储双杰, 彭俊, 胡广魁 |
|
Effect of Dew Point on Selective Oxidation and Decarburization of 0.2%C-1.5%Si-2.5%Mn High Strength Steel Sheet During Continuous Annealing |
| JIN Xinyan, CHU Shuangjie, PENG Jun, HU Guangkui |
| 图9 露点为+10℃退火试样上3个不同区域(见图8a)元素面分布 |
| Fig.9 EDS elemental mapping of three different areas (in Fig.8a) on the sample annealed at dew point of +10oC (a) upper zone (b) middle zone (c) bottom zone |
|
|