电弧熔丝增材制造2Cr13合金组织与性能各向异性行为
Anisotropy in Microstructures and Mechanical Properties of 2Cr13 Alloy Produced by Wire Arc Additive Manufacturing
(a) 550oC (b) 180oC (c) 150oC (d) 110oC
电弧熔丝增材制造2Cr13合金组织与性能各向异性行为 |
| 葛进国, 卢照, 何思亮, 孙妍, 殷硕 |
|
Anisotropy in Microstructures and Mechanical Properties of 2Cr13 Alloy Produced by Wire Arc Additive Manufacturing |
| GE Jinguo, LU Zhao, HE Siliang, SUN Yan, YIN Shuo |
| 图11 2Cr13沉积件中间部位沿沉积高度方向的硬度曲线 |
| Fig.11 Microhardness curves of WAAM 2Cr13 parts along the building direction across several layers in the middle region (As-QTed BM: 2Cr13 base metal after quenching and tempering treatment) (a) 550oC (b) 180oC (c) 150oC (d) 110oC |
|
|