电弧熔丝增材制造2Cr13合金组织与性能各向异性行为
Anisotropy in Microstructures and Mechanical Properties of 2Cr13 Alloy Produced by Wire Arc Additive Manufacturing
(a, b) 550oC (c, d) 180oC (e, f) 150oC (g, h) 110oC
电弧熔丝增材制造2Cr13合金组织与性能各向异性行为 |
| 葛进国, 卢照, 何思亮, 孙妍, 殷硕 |
|
Anisotropy in Microstructures and Mechanical Properties of 2Cr13 Alloy Produced by Wire Arc Additive Manufacturing |
| GE Jinguo, LU Zhao, HE Siliang, SUN Yan, YIN Shuo |
| 图5 2Cr13沉积件中间层组织形貌的OM像 |
| Fig.5 Low (a, c, e, g) and locally high (b, d, f, h) magnified OM images in the middle layer of WAAM 2Cr13 parts (M—martensite, G.B.—grain boundary) (a, b) 550oC (c, d) 180oC (e, f) 150oC (g, h) 110oC |
|
|