电弧熔丝增材制造2Cr13合金组织与性能各向异性行为
Anisotropy in Microstructures and Mechanical Properties of 2Cr13 Alloy Produced by Wire Arc Additive Manufacturing
电弧熔丝增材制造2Cr13合金组织与性能各向异性行为 |
| 葛进国, 卢照, 何思亮, 孙妍, 殷硕 |
|
Anisotropy in Microstructures and Mechanical Properties of 2Cr13 Alloy Produced by Wire Arc Additive Manufacturing |
| GE Jinguo, LU Zhao, HE Siliang, SUN Yan, YIN Shuo |
| 图4 2Cr13沉积件在不同层间停留温度下的XRD谱 |
| Fig.4 XRD spectra of WAAM 2Cr13 parts with the interlayer dwelling temperatures of 550oC (a), 180oC (b), 150oC (c), and 110oC (d) (Inset in Fig.4a shows the austenitic diffraction peak; F—ferrite, γ—austenite) |
|
|