快速凝固Ti-Al-Nb合金B2相形成机制与显微力学性能
Formation Mechanism of B2 Phase and Micro-Mechanical Property of Rapidly Solidified Ti-Al-Nb Alloy
(a) 740 μm (b) 417 μm (c) 206 μm (d) 181 μm
快速凝固Ti-Al-Nb合金B2相形成机制与显微力学性能 |
| 梁琛, 王小娟, 王海鹏 |
|
Formation Mechanism of B2 Phase and Micro-Mechanical Property of Rapidly Solidified Ti-Al-Nb Alloy |
| LIANG Chen, WANG Xiaojuan, WANG Haipeng |
| 图5 自由落体条件下不同直径Ti53Al22Nb25合金液滴的凝固组织演变 |
| Fig.5 Microstructure evolutions of rapidly solidified Ti53Al22Nb25 alloy droplets with different diameters (a) 740 μm (b) 417 μm (c) 206 μm (d) 181 μm |
|
|