热处理温度对Ti0.5Zr1.5NbTa0.5Sn0.2 高熵合金组织结构与力学性能的影响 |
韩林至, 牟娟, 周永康, 朱正旺, 张海峰 |
Effect of Heat Treatment Temperature on Microstructure and Mechanical Properties of Ti0.5Zr1.5NbTa0.5Sn0.2 High-Entropy Alloy |
HAN Linzhi, MU Juan, ZHOU Yongkang, ZHU Zhengwang, ZHANG Haifeng |
图4 不同状态Ti0.5Zr1.5NbTa0.5Sn0.2高熵合金的EDS面分布图 |
Fig.4 EDS mapping results of components in the Ti0.5Zr1.5NbTa0.5Sn0.2 HEA with different states (a) as-cast (b) 800oC, quenching (c) 1000oC, quenching (d) 1200oC, quenching (e) 1400oC, quenching |
![]() |