喷射成形过共晶AlSiCuMg合金的固溶行为
Solution Behavior of Spray-Formed Hypereutectic AlSiCuMg Alloy
(a) hardness of different solution temperatures (solution time is 2 h)
(b) hardness of different solution time (solution temperature is 515℃)
喷射成形过共晶AlSiCuMg合金的固溶行为 |
| 冯迪, 朱田, 臧千昊, 李胤樹, 范曦, 张豪 |
|
Solution Behavior of Spray-Formed Hypereutectic AlSiCuMg Alloy |
| FENG Di, ZHU Tian, ZANG Qianhao, LEE Yunsoo, FAN Xi, ZHANG Hao |
| 图6 不同固溶工艺下的硬度对比 |
| Fig.6 The hardness comparison between different solution treatments (a) hardness of different solution temperatures (solution time is 2 h) (b) hardness of different solution time (solution temperature is 515℃) |
|
|