淬火速率对7136铝合金应力腐蚀开裂敏感性的影响
Effect of Quenching Rate on Stress Corrosion Cracking Susceptibility of 7136 Aluminum Alloy
淬火速率对7136铝合金应力腐蚀开裂敏感性的影响 |
| 马志民, 邓运来, 刘佳, 刘胜胆, 刘洪雷 |
|
Effect of Quenching Rate on Stress Corrosion Cracking Susceptibility of 7136 Aluminum Alloy |
| MA Zhimin, DENG Yunlai, LIU Jia, LIU Shengdan, LIU Honglei |
| 图15 淬火速率为5.3和1.8℃/s时7136铝合金试样中不同无沉淀析出带宽度的晶界和亚晶界的比例 |
| Fig.15 Proportions of grain boundaries and sub-grain boundaries with different PFZ widths in 7136 aluminum alloy samples under quenching rates of 5.3 and 1.8oC/s |
|
|