高温低周疲劳下C-HRA-5奥氏体耐热钢中孪晶界演变
Twin Boundary Evolution Under Low-Cycle Fatigue of C-HRA-5 Austenitic Heat-Resistant Steel at High Temperature
(a) precipitates along the CTBs (b) precipitates along the ITBs
高温低周疲劳下C-HRA-5奥氏体耐热钢中孪晶界演变 |
| 周红伟, 高建兵, 沈加明, 赵伟, 白凤梅, 何宜柱 |
|
Twin Boundary Evolution Under Low-Cycle Fatigue of C-HRA-5 Austenitic Heat-Resistant Steel at High Temperature |
| ZHOU Hongwei, GAO Jianbing, SHEN Jiaming, ZHAO Wei, BAI Fengmei, HE Yizhu |
| 图7 C-5钢在700℃、εt = 0.5%下TBs处析出相的SEM像 |
| Fig.7 SEM images of the precipitates at TBs in C-5 steel with εt = 0.5% at 700oC (a) precipitates along the CTBs (b) precipitates along the ITBs |
|
|