290℃氩离子辐照对Fe-Cu合金微观组织的影响
Effects of Ar Ion Irradiation on Microstructure of Fe-Cu Alloys at 290oC
(a) 100-200 nm (b) 200-300 nm (c) 300-400 nm (d) 400-500 nm (e) 500-600 nm
(f) 600-700 nm (g) 700-800 nm (h) 800-900 nm (i) 900-1000 nm
290℃氩离子辐照对Fe-Cu合金微观组织的影响 |
| 朱小绘, 刘向兵, 王润中, 李远飞, 刘文庆 |
|
Effects of Ar Ion Irradiation on Microstructure of Fe-Cu Alloys at 290oC |
| ZHU Xiaohui, LIU Xiangbing, WANG Runzhong, LI Yuanfei, LIU Wenqing |
| 图3 氩离子辐照后Fe-Cu合金距辐照表面不同深度处的Cu原子分布 |
| Fig.3 Cu atom distributions of Ar ions irradiated Fe-Cu alloys as a function of depth (a) 100-200 nm (b) 200-300 nm (c) 300-400 nm (d) 400-500 nm (e) 500-600 nm (f) 600-700 nm (g) 700-800 nm (h) 800-900 nm (i) 900-1000 nm |
|
|