MoNb改性FeCrAl不锈钢高温组织演变和力学性能
Microstructure Evolution at Elevated Temperature and Mechanical Properties of MoNb-Modified FeCrAl Stainless Steel
MoNb改性FeCrAl不锈钢高温组织演变和力学性能 |
| 温冬辉, 姜贝贝, 王清, 李相伟, 张鹏, 张书彦 |
|
Microstructure Evolution at Elevated Temperature and Mechanical Properties of MoNb-Modified FeCrAl Stainless Steel |
| WEN Donghui, JIANG Beibei, WANG Qing, LI Xiangwei, ZHANG Peng, ZHANG Shuyan |
| 图7 800℃、24 h时效后的C35MN合金经过1000℃、1 h退火处理后的TEM明场像和选区电子衍射(SAED)花样 |
| Fig.7 TEM bright-field images (a-c) and SAED pattern (inset) of the C35MN alloy annealed at 1000oC, 1 h after 800oC, 24 h aging |
|
|