MoNb改性FeCrAl不锈钢高温组织演变和力学性能
Microstructure Evolution at Elevated Temperature and Mechanical Properties of MoNb-Modified FeCrAl Stainless Steel
MoNb改性FeCrAl不锈钢高温组织演变和力学性能 |
| 温冬辉, 姜贝贝, 王清, 李相伟, 张鹏, 张书彦 |
|
Microstructure Evolution at Elevated Temperature and Mechanical Properties of MoNb-Modified FeCrAl Stainless Steel |
| WEN Donghui, JIANG Beibei, WANG Qing, LI Xiangwei, ZHANG Peng, ZHANG Shuyan |
| 图5 800℃、24 h时效后的C35MN合金分别经过1000、1100和1200℃退火1 h处理后微观组织的OM和SEM像 |
| Fig.5 OM (a, c, e) and SEM (b, d, f) images of the C35MN alloy annealed at 1000oC, 1 h (a, b), 1100oC, 1 h (c, d), and 1200oC, 1 h (e, f) after 800oC, 24 h aging |
|
|