粉末高温合金FGH4096的疲劳小裂纹扩展行为 |
杨秦政, 杨晓光, 黄渭清, 石多奇 |
Propagation Behaviors of Small Cracks in Powder Metallurgy Nickel-Based Superalloy FGH4096 |
YANG Qinzheng, YANG Xiaoguang, HUANG Weiqing, SHI Duoqi |
图5 RL试样左侧主裂纹停滞与二次裂纹萌生过程 |
Fig.5 Stagnation of the left main crack and the initiation of the secondary crack in RL specimen recorded by the experimental system (a-c) and the associated SEM image (d) (N—number of cycle) (a) the main crack was stagnated at N = 1.895 × 105 cyc (b) the secondary crack was initiated at N = 1.955 × 105 cyc (c) the secondary crack connected with the main crack at N = 2.005 × 105 cyc (d) SEM image of the main area in Figs.5a-c |