不同服役条件下FGH96合金的蠕变特征
Creep Behavior of FGH96 Superalloy at Different Service Conditions
(a) 650oC, 690 MPa (b) 750oC, 690 MPa (c) 704oC, 690 MPa (d) 704oC, 810 MPa
不同服役条件下FGH96合金的蠕变特征 |
| 彭子超, 刘培元, 王旭青, 罗学军, 刘健, 邹金文 |
|
Creep Behavior of FGH96 Superalloy at Different Service Conditions |
| PENG Zichao, LIU Peiyuan, WANG Xuqing, LUO Xuejun, LIU Jian, ZOU Jinwen |
| 图9 不同温度和应力条件下FGH96合金的蠕变断裂源区形貌 |
| Fig.9 Fractographs of primary stages of FGH96 superalloy tested at different temperatures and stresses (a) 650oC, 690 MPa (b) 750oC, 690 MPa (c) 704oC, 690 MPa (d) 704oC, 810 MPa |
|
|