不同服役条件下FGH96合金的蠕变特征
Creep Behavior of FGH96 Superalloy at Different Service Conditions
(a) 690 MPa (b) 720 MPa (c) 750 MPa (d) 780 MPa (e) 810 MPa
不同服役条件下FGH96合金的蠕变特征 |
| 彭子超, 刘培元, 王旭青, 罗学军, 刘健, 邹金文 |
|
Creep Behavior of FGH96 Superalloy at Different Service Conditions |
| PENG Zichao, LIU Peiyuan, WANG Xuqing, LUO Xuejun, LIU Jian, ZOU Jinwen |
| 图5 704℃、不同加载应力条件下经过1.0%蠕变变形的FGH96合金局域取向差(KAM)和反极图(IPF)分析 |
| Fig.5 Kernel average misorientation (KAM) maps and inverse pole figures (IPFs) of FGH96 alloy with 1.0% crept strain under various loading stresses at 704oC (a) 690 MPa (b) 720 MPa (c) 750 MPa (d) 780 MPa (e) 810 MPa |
|
|