热处理对一种双峰晶粒结构超低碳9Cr-ODS钢显微组织与力学性能的影响

张家榕, 李艳芬, 王光全, 包飞洋, 芮祥, 石全强, 严伟, 单以银, 杨柯

Effects of Heat Treatment on Microstructure and Mechanical Properties of a Bimodal Grain Ultra-Low Carbon 9Cr-ODS Steel

ZHANG Jiarong, LI Yanfen, WANG Guangquan, BAO Feiyang, RUI Xiang, SHI Quanqiang, YAN Wei, SHAN Yiyin, YANG Ke

表 1 超低碳9Cr-ODS (氧化物弥散强化)钢的热处理制度

Table 1 Heat treatments design for ultra-low carbon 9Cr-ODS steel

Normalizing process Tempering process 1050oC, 1 h, AC 700oC, 1 h, AC or 750oC, 1 h, AC or 800oC, 1 h, AC 1100oC, 1 h, AC 700oC, 1 h, AC or 750oC, 1 h, AC or 800oC, 1 h, AC 1150oC, 1 h, AC 700oC, 1 h, AC or 750oC, 1 h, AC or 800oC, 1 h, AC 1200oC, 1 h, AC 700oC, 1 h, AC or 750oC, 1 h, AC or 800oC, 1 h, AC