热处理对一种双峰晶粒结构超低碳9Cr-ODS钢显微组织与力学性能的影响

张家榕, 李艳芬, 王光全, 包飞洋, 芮祥, 石全强, 严伟, 单以银, 杨柯

Effects of Heat Treatment on Microstructure and Mechanical Properties of a Bimodal Grain Ultra-Low Carbon 9Cr-ODS Steel

ZHANG Jiarong, LI Yanfen, WANG Guangquan, BAO Feiyang, RUI Xiang, SHI Quanqiang, YAN Wei, SHAN Yiyin, YANG Ke

图4 超低碳9Cr-ODS钢分别经不同热处理工艺后的OM像

Fig.4 OM images of ultra-low carbon 9Cr-ODS steel under different heat treatmens (a) 1050oC, 1 h, AC + 750oC, 1 h, AC (b) 1050oC, 1 h, AC + 800oC, 1 h, AC (c) 1100oC, 1 h, AC + 750oC, 1 h, AC (d) 1100oC, 1 h, AC + 800oC, 1 h, AC (e) 1200oC, 1 h, AC + 750oC, 1 h, AC (f) 1200oC, 1 h, AC + 800 oC, 1 h, AC