添加Ti对Fe22Cr5Al3Mo合金在500℃过热蒸汽中腐蚀行为的影响 |
|||||||||||||||||||||
| 孙蓉蓉, 姚美意, 林晓冬, 张文怀, 仇云龙, 胡丽娟, 谢耀平, 杨健, 董建新, 成国光 | |||||||||||||||||||||
|
Effect of Ti on the Corrosion Behavior of Fe22Cr5Al3Mo Alloy in 500oC Superheated Steam |
|||||||||||||||||||||
| SUN Rongrong, YAO Meiyi, LIN Xiaodong, ZHANG Wenhuai, QIU Yunlong, HU Lijuan, XIE Yaoping, YANG Jian, DONG Jianxin, CHENG Guoguang | |||||||||||||||||||||
| 表6 0Ti、0.5Ti和1.0Ti合金在500℃、10.3 MPa过热蒸汽中腐蚀500 h时铁氧化物膜、铬氧化物膜、铝氧化物膜以及Cr和Al的混合氧化物区的厚度 (nm) |
|||||||||||||||||||||
| Table 6 Average thicknesses of iron oxide film, chromium oxide film, aluminum oxide film, and overlap area formed on the 0Ti, 0.5Ti, and 1.0Ti alloys corroded in 500oC and 10.3 MPa superheated steam for 500 h |
|||||||||||||||||||||
|
|||||||||||||||||||||