微弧氧化6082-T6铝合金的高周疲劳性能及残余应力松弛机理
High-Cycle Fatigue Properties and Residual Stress Relaxation Mechanism of Micro-Arc Oxidation 6082-T6 Aluminum Alloy
(a) UP sample (cyclic stress: 220 MPa) (b) MAO sample (cyclic stress: 180 MPa)
微弧氧化6082-T6铝合金的高周疲劳性能及残余应力松弛机理 |
| 苏凯新, 张继旺, 张艳斌, 闫涛, 李行, 纪东东 |
|
High-Cycle Fatigue Properties and Residual Stress Relaxation Mechanism of Micro-Arc Oxidation 6082-T6 Aluminum Alloy |
| SU Kaixin, ZHANG Jiwang, ZHANG Yanbin, YAN Tao, LI Hang, JI Dongdong |
| 图8 UP和MAO试样的断口形貌 (a) UP sample (cyclic stress: 220 MPa) (b) MAO sample (cyclic stress: 180 MPa) |
| Fig.8 Fracture morphologies of UP and MAO samples |
|
|