(Fe0.33Co0.33Ni0.33)84 -x Cr8Mn8B x 高熵非晶合金薄带的结构特征及其晶化行为
张金勇1,2(
), 赵聪聪1, 吴宜谨1, 陈长玖1, 陈正1, 沈宝龙1()
), 赵聪聪1, 吴宜谨1, 陈长玖1, 陈正1, 沈宝龙1()
Structural Characteristic and Crystallization Behavior of the (Fe0.33Co0.33Ni0.33)84 -x Cr8Mn8B x High-Entropy-Amorphous Alloy Ribbons
ZHANG Jinyong1,2(), ZHAO Congcong1, WU Yijin1, CHEN Changjiu1, CHEN Zheng1, SHEN Baolong1()
), ZHAO Congcong1, WU Yijin1, CHEN Changjiu1, CHEN Zheng1, SHEN Baolong1()
图9. 未经退火处理的11B合金薄带弯折180°后折痕处的SEM像及未经退火处理的10B~18B合金薄带的Vickers硬度随B元素含量的变化
Fig.9. SEM images of 11B alloy ribbons after bending 180° with different magnifications (a), and Vickers hardness of 10B-18B as-spun alloy ribbons vs the B content (b)