(Fe0.33Co0.33Ni0.33)84 -x Cr8Mn8B x 高熵非晶合金薄带的结构特征及其晶化行为
张金勇1,2(
), 赵聪聪1, 吴宜谨1, 陈长玖1, 陈正1, 沈宝龙1()
), 赵聪聪1, 吴宜谨1, 陈长玖1, 陈正1, 沈宝龙1()
Structural Characteristic and Crystallization Behavior of the (Fe0.33Co0.33Ni0.33)84 -x Cr8Mn8B x High-Entropy-Amorphous Alloy Ribbons
ZHANG Jinyong1,2(), ZHAO Congcong1, WU Yijin1, CHEN Changjiu1, CHEN Zheng1, SHEN Baolong1()
), ZHAO Congcong1, WU Yijin1, CHEN Changjiu1, CHEN Zheng1, SHEN Baolong1()
图6. 11B非晶合金薄带经725 K退火1800 s后的TEM像、SAED花样和HRTEM像
Fig.6. Bright-field (a) and dark-field (b) TEM images, SAED pattern (c), and HRTEM image (d) of 11B amorphous alloy ribbon after annealing at 725 K for 1800 s (The inset in Fig.6d is the corresponding fast Fourier transform (FFT) diffractogram, d—interplanar spacing)