Structural Characteristic and Crystallization Behavior of the (Fe0.33Co0.33Ni0.33)84 -x Cr8Mn8B x High-Entropy-Amorphous Alloy Ribbons
ZHANG Jinyong1,2(), ZHAO Congcong1, WU Yijin1, CHEN Changjiu1, CHEN Zheng1, SHEN Baolong1()
), ZHAO Congcong1, WU Yijin1, CHEN Changjiu1, CHEN Zheng1, SHEN Baolong1()
图3. 11B~18B合金薄带的DSC曲线及晶化峰起始温度随B元素含量变化
Fig.3. DSC curves of 11B-18B as-spun alloy ribbons (a) and changes in the onset temperatures of the first and second exotherms (Tx1 and Tx2) with B content (b) (Heating rate is 0.67 K/s, Tg—the glass transition temperature)