磁场与晶粒尺寸协同作用对马氏体形核及变体选择的影响 |
原家华, 张秋红, 王金亮, 王灵禺, 王晨充, 徐伟 |
Synergistic Effect of Magnetic Field and Grain Size on Martensite Nucleation and Variant Selection |
YUAN Jiahua, ZHANG Qiuhong, WANG Jinliang, WANG Lingyu, WANG Chenchong, XU Wei |
图2 在1和9 T磁场下不同晶粒尺寸SUS321不锈钢试样在降温过程中α′-马氏体的含量变化曲线 |
Fig.2 Variation curves of martensite content under 1 and 9 T magnetic fields of SUS321 stainless steel with different gain sizes during cooling (a) 6.6 μm (b) 29.3 μm (c) 203 μm |
![]() |