非晶态U60Fe27.5Al12.5 合金的晶化动力学行为
韩录会, 柯海波, 张培, 桑革, 黄火根

Kinetic Crystallization Behavior of Amorphous U60Fe27.5Al12.5 Alloy
HAN Luhui, KE Haibo, ZHANG Pei, SANG Ge, HUANG Huogen
表3 部分非晶合金的特征温度与晶化动力学参数[19,20,23~32]
Table 3 Characteristic temperatures and crystallization kinetic parameters of some amorphous alloys[19,20,23-32]
Metallic glassTg / KTx / K

Eg

kJ·min-1

Ex or Ep / (kJ·min-1)nRef.
Zr41Ti14Cu12.5Ni10Be22.5

626

(10 K·min-1)

692

(10 K·min-1)

~557 (Ki)~192 (Ki)-[23]
Zr55Cu30Al10Ni5

~681

(20 K·min-1)

~764

(20 K·min-1)

894 (Ki)

230 (Ki)

245 (JMA, Iso)

2.6-3.1

(JMA, Iso)

[19]
Cu47Ti33Zr11Ni8Si1

691

(20 K·min-1)

752

(20 K·min-1)

-

~339 (Ki)

~354 (JMA, Iso)

2.8-3.5

(JMA, Iso)

[24]
Co43Fe20Ta5.5B31.5

~940

(25 K·min-1)

~980

(25 K·min-1)

-

437~595 (Ki)

432~582 (Oz)

-[25]
Cu46Zr45Al7Y2-

~741

(10 K·min-1)

-

340~361 (Ki)

484 (JMA, Iso)

2.4-2.7

(JMA, Iso)

[20]
Cu15(As2Se3)85

~463

(20 K·min-1)

~557

(20 K·min-1)

~282 (Ki)~172 (Ki)

~3.8

(JMA, Non-iso)

[26]
Zr60Cu20Al10Ni10

~670

(20 K·min-1)

~740

(20 K·min-1)

-

202~327 (Ki)

215~339 (Oz)

1.5-15.7

(JMA, Non-iso)

[27]
Ca65Mg15Zn20

~375

(20 K·min-1)

~408

(20 K·min-1)

~148 (Ki)

116~124 (Ki)

147~178 (JMA, Iso)

2.0-2.7

(JMA, Iso)

[28]
Cu54Zr37Ti8In1

700

(25 K·min-1)

729

(25 K·min-1)

~321 (Ki)331~392 (Ki)

2.0-4.5

(JMA, Non-iso)

[29]
Zr46Cu38Ag8Al8-

~784

(20 K·min-1)

-

~310 (Ki)

~451 (JMA, Iso)

4.1-4.8

(JMA, Iso)

[30]

Ti16.7Zr16.7Hf16.7Cu16.7

Ni16.7Be16.7

~700

(20 K·min-1)

~740

(20 K·min-1)

~332 (Ki)

215~246 (Ki)

~260 (JMA, Iso)

1.8-2.1

(JMA, Iso)

[31]
U64Co28.5Al7.5

616

(20 K·min-1)

638

(20 K·min-1)

338 (Ki)200~250 (Ki)

1.5-11.0

(JMA, Non-iso)

[32]