利用ZrO2 固体电解质研究Na3AlF6-SiO2 熔盐中的电沉积
|
高运明, 何林, 秦庆伟, 李光强
|
ZrO2 Solid Electrolyte Aided Investigation on Electrodeposition in Na3AlF6-SiO2 Melt
|
GAO Yunming, HE Lin, QIN Qingwei, LI Guangqiang
|
|
表4 对应于图7中各点位的EDS结果
|
Table 4 EDS results corresponding to the points in Fig.7
|
|
Point | Mass fraction of element / % | Possible phase |
---|
(atomic fraction / %) |
---|
| | Zr | Si | Au | O | | | 1 | 74.03 | | | 25.97 | ZrO2 | | (33.33) | | | (66.67) | | 2 | 74.03 | | | 25.97 | ZrO2 | | (33.33) | | | (66.67) | | 3 | 41.77 | 11.15 | 41.39 | | Zr5Si4(s) | | (29.77) | (25.82) | (13.66) | | | 4 | 40.16 | 11.07 | 42.32 | | Zr5Si4(s) | | (27.76) | (24.84) | (13.55) | | | 5 | 42.11 | 11.46 | 40.46 | | Zr5Si4(s) | | (29.36) | (25.95) | (13.07) | | | 6 | 41.86 | 10.85 | 40.07 | | Zr5Si4(s) | | (27.82) | (23.41) | (12.33) | | |
|
|
|