利用ZrO2 固体电解质研究Na3AlF6-SiO2 熔盐中的电沉积
|
高运明, 何林, 秦庆伟, 李光强
|
ZrO2 Solid Electrolyte Aided Investigation on Electrodeposition in Na3AlF6-SiO2 Melt
|
GAO Yunming, HE Lin, QIN Qingwei, LI Guangqiang
|
|
表3 对应于图6中各点位的EDS结果
|
Table 3 EDS results corresponding to the points in Fig.6
|
|
Point | Mass fraction of element / % | Possible phase |
---|
(atomic fraction / %) |
---|
| | O | Ir | Zr | Si | Al | Fe | Au | | | 1 | 7.61 | 19.43 | 32.85 | | | 1.76 | 38.36 | Fe-Ir, ZrO2 | | (40.88) | (8.69) | (30.97) | | | (2.71) | (16.75) | | 2 | | 55.56 | | | | | 44.44 | Ir | | | (56.16) | | | | | (43.84) | | 3 | | 72.67 | | 1.31 | | 13.22 | 12.79 | Fe-Si-Ir | | | (52.04) | | (6.44) | | (32.58) | (8.94) | | 4 | | 48.14 | | 1.82 | | | 50.04 | Ir-Si | | | (43.99) | | (11.39) | | | (44.62) | | 5 | | 48.74 | | 2.37 | | | 48.89 | Ir-Si | | | (43.27) | | (14.37) | | | (42.35) | | 6 | | 42.81 | | 6.02 | | | 51.16 | Ir-Si | | | (31.96) | | (30.77) | | | (37.27) | | 7 | | | 44.33 | 11.81 | | | 43.86 | Zr5Si4 | | | | (43.04) | (37.24) | | | (19.72) | | 8 | | 40.30 | 2.59 | 6.90 | 1.17 | | 49.04 | Si x Al y Zr z Ir m | | | (27.01) | (3.66) | (31.64) | (5.61) | | (32.08) | | 9 | | 44.83 | | 5.45 | 0.32 | | 49.40 | Si x Al y Ir z | | | (33.80) | | (28.13) | (1.73) | | (36.34) | | 10 | | 39.00 | 6.98 | 6.14 | 0.22 | | 47.66 | Si x Al y Zr z Ir m | | | (27.12) | (10.22) | (29.24) | (1.07) | | (32.35) | | 11 | | 44.51 | | 5.62 | 0.38 | | 49.50 | Si x Al y Ir z | | | (33.22) | | (28.70) | (2.02) | | (36.05) | |
|
|
|