不同Cr含量的奥氏体不锈钢在700℃煤灰/高硫烟气环境中的腐蚀行为
Corrosion Behavior of Austenitic Stainless Steel with Different Cr Contents in 700oC Coal Ash/High Sulfur Flue-Gas Environment
(a) low Cr alloy (b) medium Cr alloy (c) high Cr alloy
不同Cr含量的奥氏体不锈钢在700℃煤灰/高硫烟气环境中的腐蚀行为 |
| 曹超, 蒋成洋, 鲁金涛, 陈明辉, 耿树江, 王福会 |
|
Corrosion Behavior of Austenitic Stainless Steel with Different Cr Contents in 700oC Coal Ash/High Sulfur Flue-Gas Environment |
| CAO Chao, JIANG Chengyang, LU Jintao, CHEN Minghui, GENG Shujiang, WANG Fuhui |
| 图5 3种样品在700℃腐蚀1000 h后的截面形貌 |
| Fig.5 The cross-sectional morphologies of the three test samples after corrosion at 700oC for 1000 h (a) low Cr alloy (b) medium Cr alloy (c) high Cr alloy |
|
|