Multimodal Microstructure of Mg-Gd-Y Alloy Through an Integrated Simulation of Process-Structure-Property
LI Shaojie, JIN Jianfeng, SONG Yuhao, WANG Mingtao, TANG Shuai, ZONG Yaping, QIN Gaowu
图10 经过723 K退火90 min后,有/无第二相粒子的GW83K镁合金有限元模拟结果
Fig.10 Mechanical responses from finite element model for GW83K Mg alloy with and without the 2nd phase particles from model A, B, and C after annealing at 723 K for 90 min (a) and EQV. strain contours of models A and C under fractured strain (b) (Model A is the FE simulation from microstructure with the 2nd phase particles after annealing, model B is from microstructure without the 2nd phase particles after annealing, and model C is from Fig.10a without the 2nd phase particles)