超细晶铁素体-马氏体钢的高温氧化成膜特性及其对Pb-Bi腐蚀行为的影响
Oxide Scale Formation on Ultrafine-Grained Ferritic-Martensitic Steel During Pre-Oxidation and Its Effect on the Corrosion Performance in Stagnant Liquid Pb-Bi Eutectic
超细晶铁素体-马氏体钢的高温氧化成膜特性及其对Pb-Bi腐蚀行为的影响 |
| 陈胜虎, 戎利建 |
|
Oxide Scale Formation on Ultrafine-Grained Ferritic-Martensitic Steel During Pre-Oxidation and Its Effect on the Corrosion Performance in Stagnant Liquid Pb-Bi Eutectic |
| CHEN Shenghu, RONG Lijian |
| 图6 未预氧化处理与预氧化处理的94%变形量样品经550℃饱和氧LBE腐蚀500和2000 h后氧化膜截面形貌的BSE像 |
| Fig.6 Back scattered electron (BSE) cross-sectional morphologies of cold rotary-swaged 9Cr2WVTa ferritic-martensitic steels at deformation rate of 94% without (a, b) and with (c, d) pre-oxidation treatment after exposure for 500 h (a, c) and 2000 h (b, d) to stagnant oxygen-saturated LBE at 550oC (Inset in Fig.6a shows the high magnification image of oxide scale) |
|
|