真空渗碳处理齿轮钢的氢脆敏感性
Hydrogen Embrittlement Behavior of a Vacuum-Carburized Gear Steel
(a) before SSRT (b) after SSRT (c) hydrogen rich and crack initiation and propagation
真空渗碳处理齿轮钢的氢脆敏感性 |
| 肖娜, 惠卫军, 张永健, 赵晓丽 |
|
Hydrogen Embrittlement Behavior of a Vacuum-Carburized Gear Steel |
| XIAO Na, HUI Weijun, ZHANG Yongjian, ZHAO Xiaoli |
| 图12 渗碳试样的氢脆断裂机理示意图 (a) before SSRT (b) after SSRT (c) hydrogen rich and crack initiation and propagation |
| Fig.12 Schematics of the hydrogen embrittlement (HE) mechanism of the carburized specimen (A—maximum diffusion distance, B—crack, C—interface between the case layer and the core matrix) |
|
|