真空渗碳处理齿轮钢的氢脆敏感性
Hydrogen Embrittlement Behavior of a Vacuum-Carburized Gear Steel
(a) low magnification (b) crack initiation region (c) crack propagation region (d) fast fracture region
真空渗碳处理齿轮钢的氢脆敏感性 |
| 肖娜, 惠卫军, 张永健, 赵晓丽 |
|
Hydrogen Embrittlement Behavior of a Vacuum-Carburized Gear Steel |
| XIAO Na, HUI Weijun, ZHANG Yongjian, ZHAO Xiaoli |
| 图8 渗碳试样未充氢时的SSRT断口SEM像 (a) low magnification (b) crack initiation region (c) crack propagation region (d) fast fracture region |
| Fig.8 SEM images showing the fracture surfaces of the carburized specimen without hydrogen-charging |
|
|