耦合热力学相变路径预测Fe-C包晶合金宏观偏析
Prediction of Macrosegregation of Fe-C Peritectic Alloy Ingot Through Coupling with Thermodynamic Phase Transformation Path
耦合热力学相变路径预测Fe-C包晶合金宏观偏析 |
| 冯苗苗, 张红伟, 邵景霞, 李铁, 雷洪, 王强 |
|
Prediction of Macrosegregation of Fe-C Peritectic Alloy Ingot Through Coupling with Thermodynamic Phase Transformation Path |
| FENG Miaomiao, ZHANG Hongwei, SHAO Jingxia, LI Tie, LEI Hong, WANG Qiang |
| 图8 采用LR-TEC和LR Analytical模型模拟的Sn-5%Pb合金凝固进行到400 s时溶质Pb的相对溶质成分分布[(c - c0) / c0] × 100 |
| Fig.8 Distributions of relative solute concentration [(c - c0) / c0] × 100 for solute Pb solidified at 400 s for Sn-5%Pb alloy predicted by LR-TEC (a) and LR Analytical (b) models |
|
|