物理气相沉积制备金属玻璃薄膜及其力学性能的样品尺寸效应
Magnetron Sputtering Metal Glass Film Preparation and the “Specimen Size Effect” of the Mechanical Property
物理气相沉积制备金属玻璃薄膜及其力学性能的样品尺寸效应 |
| 曹庆平, 吕林波, 王晓东, 蒋建中 |
|
Magnetron Sputtering Metal Glass Film Preparation and the “Specimen Size Effect” of the Mechanical Property |
| CAO Qingping, LV Linbo, WANG Xiaodong, JIANG Jianzhong |
| 图12 厚度为5 μm的Zr65Ni35金属玻璃薄膜样品在FIB处理0、10、20和30 min的压痕形貌SEM像，及剪切带数量与硬度随处理时间的变化[ |
| Fig.12 Indentation morphology SEM images of Zr65Ni35 metallic glass thin films samples (thickness of 5 μm) in the focused ion beam (FIB) processing for 0 min (a), 10 min (b), 20 min (c), and 30 min (d); and average number of shear band and hardness reduction with the change of milling time (e)[ |
|
|