喷涂工艺对Ta2O5原位复合钽基纳米晶涂层微观结构及摩擦磨损性能的影响
李晓倩, 王富国, 梁爱民

Effect of Spraying Process on Microstructure and Tribological Properties of Ta2O5 In Situ Composite Nanocrystalline Ta-Based Coatings
LI Xiaoqian, WANG Fuguo, LIANG Aimin
表2 No.1~No.7钽基涂层表面2种物相XRD峰的强度比
Table 2 Intensity ratios of XRD peaks of two phases in surface layers of No.1-No.7 Ta-based coatings
CoatingITa2O5(001)/ITa(110)ITa2O5(001)/ITa(200)ITa2O5(001)/ITa(211)ITa2O5(110)/ITa(110)ITa2O5(110)/ITa(200)ITa2O5(110)/ITa(211)
No.10.0440.4160.1560.0530.5000.188
No.20.0360.2860.1140.0450.3570.143
No.30.0310.3080.1110.0310.3080.111
No.40.0470.4170.1520.0660.5830.212
No.50.0350.0350.1140.0530.4620.176
No.60.0360.0360.1180.0540.4620.176
No.70.0350.0350.1180.0450.3850.147