18.7Cr-1.0Ni-5.8Mn-0.2N节Ni型双相不锈钢的大变形热压缩软化行为
倪珂, 杨银辉(
), 曹建春, 王刘行, 刘泽辉, 钱昊
), 曹建春, 王刘行, 刘泽辉, 钱昊
Softening Behavior of 18.7Cr-1.0Ni-5.8Mn-0.2N Low Nickel-Type Duplex Stainless Steel During Hot Compression Deformation Under Large Strain
NI Ke, YANG Yinhui(), CAO Jianchun, WANG Liuhang, LIU Zehui, QIAN Hao
), CAO Jianchun, WANG Liuhang, LIU Zehui, QIAN Hao
图7. 两相及两相之和中HAGB数量随着应变速率和温度的变化
(a) 1223 K, 0.01-10 s-1(b) 0.1 s-1, 1123-1423 K
Fig.7. Number fraction variations of HAGB with the strain rate and temperature in two phases and the sum of two phases