18.7Cr-1.0Ni-5.8Mn-0.2N节Ni型双相不锈钢的大变形热压缩软化行为
倪珂, 杨银辉(
), 曹建春, 王刘行, 刘泽辉, 钱昊
), 曹建春, 王刘行, 刘泽辉, 钱昊
Softening Behavior of 18.7Cr-1.0Ni-5.8Mn-0.2N Low Nickel-Type Duplex Stainless Steel During Hot Compression Deformation Under Large Strain
NI Ke, YANG Yinhui(), CAO Jianchun, WANG Liuhang, LIU Zehui, QIAN Hao
), CAO Jianchun, WANG Liuhang, LIU Zehui, QIAN Hao
图5. 1123 K变形时双相不锈钢试样中铁素体平均晶粒尺寸与应变速率的关系
Fig.5. Relationship between average ferrite grain size and strain rate of duplex stainless steel samples deformed at 1123 K