低活化铁素体/马氏体钢组织调控及其固相连接研究进展
刘晨曦, 毛春亮, 崔雷, 周晓胜, 余黎明, 刘永长

Recent Progress in Microstructural Control and Solid-State Welding of Reduced Activation Ferritic/Martensitic Steels
LIU Chenxi, MAO Chunliang, CUI Lei, ZHOU Xiaosheng, YU Liming, LIU Yongchang
图10 不同轧制与回火工艺下RAFM钢试样的TEM像
(a, d) without rolling (b, e) rolling at 550oC with a deformation reduction of 60% and tempering at 750oC for 1.5 h (c, f) rolling at 550oC with a deformation reduction of 60% and tempering at 650oC for 5 h, and then tempering at 750oC for 1.5 h
Fig.10 TEM images of the RAFM steel sample after rolling and tempering with the different conditions for twin-jet electropolishing samples (a-c) and extraction replica samples (d-f)