高强韧钛合金组成相成分和形态的精细调控
Toughening High Strength Titanium Alloys Through Fine Tuning Phase Composition and Refining Microstructure
高强韧钛合金组成相成分和形态的精细调控 |
| 杨锐, 马英杰, 雷家峰, 胡青苗, 黄森森 |
|
Toughening High Strength Titanium Alloys Through Fine Tuning Phase Composition and Refining Microstructure |
| YANG Rui, MA Yingjie, LEI Jiafeng, HU Qingmiao, HUANG Sensen |
| 图9 Ti64合金在α + β两相区不同温度热处理后的初生α相(αp)、β转变区域(βt) Al和V元素浓度[ |
| Fig.9 Comparison of compositions in the center of primary α (αp) and β transformation (βt) between experiments (symbols) and calculations (lines) as a function of α + β solution temperature, where the measurements were made on samples after solution for 30 min and water quenching (The element contents after solution at 970oC for 16 h are also indicated in the gray rectangle)[ |
|
|