AZ31镁合金表面苯丙氨酸、甲硫氨酸和天冬酰胺诱导Ca-P涂层耐蚀性能比较
|
王雪梅, 殷正正, 于晓彤, 邹玉红, 曾荣昌
|
Comparison of Corrosion Resistance of Phenylalanine, Methionine, and Asparagine-Induced Ca-P Coatings on AZ31 Magnesium Alloys
|
WANG Xuemei, YIN Zhengzheng, YU Xiaotong, ZOU Yuhong, ZENG Rongchang
|
|
表4 图11中点1~15的EDS分析结果 (atomic fraction / %)
|
Table 4 EDS analysis results of points 1-15 in Fig.11
|
|
Point | C | N | O | Mg | Ca | P |
---|
1 | 3.98 | 1.45 | 63.07 | 14.16 | 8.72 | 8.61 | 2 | 6.02 | 1.09 | 62.60 | 15.06 | 7.62 | 7.60 | 3 | 5.79 | 0.93 | 70.34 | 10.79 | 5.20 | 6.95 | 4 | 8.20 | 1.91 | 68.69 | 5.62 | 7.70 | 7.88 | 5 | 5.75 | 1.45 | 70.74 | 1.33 | 9.04 | 11.68 | 6 | 5.29 | 1.32 | 65.10 | 3.51 | 15.99 | 8.79 | 7 | 3.42 | 1.31 | 61.38 | 5.99 | 13.20 | 14.69 | 8 | 11.40 | 4.92 | 61.09 | 3.52 | 10.20 | 8.87 | 9 | 12.38 | 5.05 | 58.08 | 2.51 | 11.36 | 10.62 | 10 | 6.45 | 1.86 | 63.70 | 3.46 | 13.96 | 10.57 | 11 | 6.96 | 1.97 | 70.64 | 2.69 | 10.55 | 7.19 | 12 | 5.61 | 1.87 | 62.78 | 3.33 | 14.22 | 12.18 | 13 | 5.36 | 1.65 | 60.92 | 3.70 | 15.83 | 12.97 | 14 | 4.92 | 1.73 | 60.67 | 3.93 | 16.60 | 12.15 | 15 | 4.84 | 1.46 | 61.37 | 2.42 | 14.84 | 15.07 |
|
|
|