锻造-增材复合制造Ti-6Al-4V合金结合区显微组织及力学性能
马健凯, 李俊杰, 王志军, 王俞鉴, 王锦程

Bonding Zone Microstructure and Mechanical Properties of Forging-Additive Hybrid Manufactured Ti-6Al-4V Alloy
MA Jiankai, LI Junjie, WANG Zhijun, WANG Yujian, WANG Jincheng
表3 不同线能量密度下锻造-增材复合制造Ti-6Al-4V合金的力学性能
Table 3 Tensile properties of the forging-additive hybrid manufactured Ti-6Al-4V alloy under different linear energy densities
SampleUTS / MPaYS / MPaEL / %
1954.64 ± 0.4861.74 ± 3.212.48 ± 2.25
2918.00 ± 8.1815.60 ± 5.512.80 ± 0.24
3915.86 ± 10.5828.23 ± 7.815.43 ± 0.45