锻造-增材复合制造Ti-6Al-4V合金结合区显微组织及力学性能 |
马健凯, 李俊杰, 王志军, 王俞鉴, 王锦程 |
Bonding Zone Microstructure and Mechanical Properties of Forging-Additive Hybrid Manufactured Ti-6Al-4V Alloy |
MA Jiankai, LI Junjie, WANG Zhijun, WANG Yujian, WANG Jincheng |
图6 不同线能量密度下锻造-增材复合制造Ti-6Al-4V合金结合区中部的显微组织 |
Fig.6 Microstructures of the middle of bonding zone in forging-additive hybrid manufactured Ti-6Al-4V alloy under linear energy densities of 100 J/mm (a), 133 J/mm (b), and 200 J/mm (c) (αs—secondary α) |
![]() |