高温时效处理对S31042耐热钢组织和蠕变性能的影响
郭倩颖1, 李彦默2, 陈斌2, 丁然1, 余黎明1, 刘永长1(
)
)
Effect of High-Temperature Ageing on Microstructure and Creep Properties of S31042 Heat-Resistant Steel
GUO Qianying1, LI Yanmo2, CHEN Bin2, DING Ran1, YU Liming1, LIU Yongchang1()
)
图10. 固溶态和时效态S31042钢在不同应力条件下蠕变试样的断口纵截面形貌
Fig.10. Creep fracture profiles on longitudinal sections of solution-treated (a-c) and ageing-treated (d-f) S31042 steel samples after creep at 700oC under 300 MPa (a, d), 250 MPa (b, e), and 220 MPa (c, f)