高温时效处理对S31042耐热钢组织和蠕变性能的影响
郭倩颖1, 李彦默2, 陈斌2, 丁然1, 余黎明1, 刘永长1(
)
)
Effect of High-Temperature Ageing on Microstructure and Creep Properties of S31042 Heat-Resistant Steel
GUO Qianying1, LI Yanmo2, CHEN Bin2, DING Ran1, YU Liming1, LIU Yongchang1()
)
图3. 固溶态和时效态S31042钢700℃、200 MPa蠕变样品中晶内析出相的TEM像、HRTEM像及SAED花样
Fig.3. TEM (a, c) and HRTEM (b) images, and SAED pattern (d) of intragranular precipitates of solution-treated (a, b) and ageing-treated (c, d) S31042 steel samples after creep at 700oC under 200 MPa for 505 h (a, b) and 354 h (c, d)