难熔高熵合金在反应堆结构材料领域的机遇与挑战
李天昕1, 卢一平1,2(
), 曹志强1, 王同敏1, 李廷举1
), 曹志强1, 王同敏1, 李廷举1
Opportunity and Challenge of Refractory High-Entropy Alloys in the Field of Reactor Structural Materials
LI Tianxin1, LU Yiping1,2(), CAO Zhiqiang1, WANG Tongmin1, LI Tingju1
), CAO Zhiqiang1, WANG Tongmin1, LI Tingju1
图8. Ti2ZrHfV0.5Mo0.2合金在不同剂量辐照前后的纳米硬度和晶格常数变化[
Fig.8. Average nanoindentation hardness vs the indentation depth (a) and variation of lattice parameter vs irradiation dose (b) for irradiated Ti2ZrHfV0.5Mo0.2 alloys at different ion doses[